BrLaO
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.145Å b=4.145Å c=7.359Å
α=90° β=90° γ=90°
ClLaO
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.119Å b=4.119Å c=6.883Å
α=90° β=90° γ=90°
ILaO
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.144Å b=4.144Å c=9.126Å
α=90° β=90° γ=90°
BrNdO
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.017Å b=4.017Å c=7.619Å
α=90° β=90° γ=90°
ClNdO
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.018Å b=4.018Å c=6.782Å
α=90° β=90° γ=90°
BrFPb
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.18Å b=4.18Å c=7.59Å
α=90° β=90° γ=90°
ClFPb
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.106Å b=4.106Å c=7.23Å
α=90° β=90° γ=90°
ClOPr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.051Å b=4.051Å c=6.810Å
α=90° β=90° γ=90°
BrOPu
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.022Å b=4.022Å c=7.571Å
α=90° β=90° γ=90°
ClOPu
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.012Å b=4.012Å c=6.792Å
α=90° β=90° γ=90°
IOPu
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.042Å b=4.042Å c=9.169Å
α=90° β=90° γ=90°
ClOSm
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=3.982Å b=3.982Å c=6.721Å
α=90° β=90° γ=90°
BrHSr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.254Å b=4.254Å c=7.290Å
α=90° β=90° γ=90°
ClHSr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.100Å b=4.100Å c=6.961Å
α=90° β=90° γ=90°
OSeTh
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.038Å b=4.038Å c=7.03Å
α=90° β=90° γ=90°
HISr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.371Å b=4.371Å c=8.450Å
α=90° β=90° γ=90°
OSTh
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=3.963Å b=3.963Å c=6.746Å
α=90° β=90° γ=90°
IOTm
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=3.895Å b=3.895Å c=9.184Å
α=90° β=90° γ=90°
OTeTh
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=4.118Å b=4.118Å c=7.549Å
α=90° β=90° γ=90°
OSU
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=3.843Å b=3.843Å c=6.694Å
α=90° β=90° γ=90°
ClOY
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 294-296
a=3.903Å b=3.903Å c=6.597Å
α=90° β=90° γ=90°
ClFeO
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 296-298
a=3.75Å b=3.3Å c=7.65Å
α=90° β=90° γ=90°
BrIO
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 296-298
a=4.049Å b=3.611Å c=8.649Å
α=90° β=90° γ=90°
ClIO
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 296-298
a=4.065Å b=3.523Å c=8.080Å
α=90° β=90° γ=90°
AlClO
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 296-298
a=3.62Å b=3.61Å c=7.67Å
α=90° β=90° γ=90°
Cl2Pb
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 298-306
a=9.030Å b=7.608Å c=4.525Å
α=90° β=90° γ=90°
F2Pb
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 298-306
a=7.63574Å b=6.42689Å c=3.89098Å
α=90° β=90° γ=90°
Br2Pb
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 298-306
a=9.466Å b=8.068Å c=4.767Å
α=90° β=90° γ=90°
CoI2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 239-444
a=3.96Å b=3.96Å c=6.65Å
α=90° β=90° γ=120°
FeI2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 239-444
a=4.04Å b=4.04Å c=6.75Å
α=90° β=90° γ=120°
GeI2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 239-444
a=4.13Å b=4.13Å c=6.79Å
α=90° β=90° γ=120°
IrTe2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 239-444
a=3.93Å b=3.93Å c=5.393Å
α=90° β=90° γ=120°
NiTe2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 239-444
a=3.861Å b=3.861Å c=5.297Å
α=90° β=90° γ=120°
PtTe2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 239-444
a=4.010Å b=4.010Å c=5.201Å
α=90° β=90° γ=120°
PtSe2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 239-444
a=3.724Å b=3.724Å c=5.062Å
α=90° β=90° γ=120°
SiTe2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 239-444
a=4.28Å b=4.28Å c=6.71Å
α=90° β=90° γ=120°
AuPb2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 239-444
a=7.31Å b=7.31Å c=5.644Å
α=90° β=90° γ=90°
CdI2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 239-444
a=4.24Å b=4.24Å c=13.67Å
α=90° β=90° γ=120°
MoS2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 280-281
a=3.1604Å b=3.1604Å c=12.295Å
α=90° β=90° γ=120°
MoTe2
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 280-281
a=3.5182Å b=3.5182Å c=13.9736Å
α=90° β=90° γ=120°
Ce
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.1612Å b=5.1612Å c=5.1612Å
α=90° β=90° γ=90°
Co
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.548Å b=3.548Å c=3.548Å
α=90° β=90° γ=90°
Ni
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.52387Å b=3.52387Å c=3.52387Å
α=90° β=90° γ=90°
Pb
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=4.9505Å b=4.9505Å c=4.9505Å
α=90° β=90° γ=90°
Pd
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.8898Å b=3.8898Å c=3.8898Å
α=90° β=90° γ=90°
Pt
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.9231Å b=3.9231Å c=3.9231Å
α=90° β=90° γ=90°
Be
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=2.2866Å b=2.2866Å c=3.5833Å
α=90° β=90° γ=120°
Cd
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=2.97887Å b=2.97887Å c=5.61765Å
α=90° β=90° γ=120°
Co
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=2.5071Å b=2.5071Å c=4.0686Å
α=90° β=90° γ=120°
Ac
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.311Å b=5.311Å c=5.311Å
α=90° β=90° γ=90°
Ag
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=4.0862Å b=4.0862Å c=4.0862Å
α=90° β=90° γ=90°
Ar
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.256Å b=5.256Å c=5.256Å
α=90° β=90° γ=90°
Au
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=4.07825Å b=4.07825Å c=4.07825Å
α=90° β=90° γ=90°
Cr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.68Å b=3.68Å c=3.68Å
α=90° β=90° γ=90°
Cu
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.61496Å b=3.61496Å c=3.61496Å
α=90° β=90° γ=90°
Fe
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.5910Å b=3.5910Å c=3.5910Å
α=90° β=90° γ=90°
Ir
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.8394Å b=3.8394Å c=3.8394Å
α=90° β=90° γ=90°
Kr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.721Å b=5.721Å c=5.721Å
α=90° β=90° γ=90°
La
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.296Å b=5.296Å c=5.296Å
α=90° β=90° γ=90°
Ne
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=4.429Å b=4.429Å c=4.429Å
α=90° β=90° γ=90°
Pr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.161Å b=5.161Å c=5.161Å
α=90° β=90° γ=90°
Pu
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=4.6370Å b=4.6370Å c=4.6370Å
α=90° β=90° γ=90°
Sc
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=4.541Å b=4.541Å c=4.541Å
α=90° β=90° γ=90°
Th
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.0843Å b=5.0843Å c=5.0843Å
α=90° β=90° γ=90°
Sr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=6.0847Å b=6.0847Å c=6.0847Å
α=90° β=90° γ=90°
Yb
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.4862Å b=5.4862Å c=5.4862Å
α=90° β=90° γ=90°
Ca
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.98Å b=3.98Å c=6.52Å
α=90° β=90° γ=120°
Cr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=2.722Å b=2.722Å c=4.427Å
α=90° β=90° γ=120°
Dy
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.5903Å b=3.5903Å c=5.6475Å
α=90° β=90° γ=120°
Er
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.550Å b=3.550Å c=5.590Å
α=90° β=90° γ=120°
Er
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.5588Å b=3.5588Å c=5.5874Å
α=90° β=90° γ=120°
Gd
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.629Å b=3.629Å c=5.796Å
α=90° β=90° γ=120°
Gd
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.6360Å b=3.6360Å c=5.7826Å
α=90° β=90° γ=120°
Hf
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.1967Å b=3.1967Å c=5.0578Å
α=90° β=90° γ=120°
Nd
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.657Å b=3.657Å c=5.902Å
α=90° β=90° γ=120°
Mg
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.20927Å b=3.20927Å c=5.21033Å
α=90° β=90° γ=120°
Ru
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=2.70389Å b=2.70389Å c=4.28168Å
α=90° β=90° γ=120°
Ti
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=2.950Å b=2.950Å c=4.686Å
α=90° β=90° γ=120°
Zn
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=2.6648Å b=2.6648Å c=4.9467Å
α=90° β=90° γ=120°
Zr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.232Å b=3.232Å c=5.147Å
α=90° β=90° γ=120°
K
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.247Å b=5.247Å c=5.247Å
α=90° β=90° γ=90°
Mo
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.1473Å b=3.1473Å c=3.1473Å
α=90° β=90° γ=90°
Na
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=4.2906Å b=4.2906Å c=4.2906Å
α=90° β=90° γ=90°
Ti
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.3065Å b=3.3065Å c=3.3065Å
α=90° β=90° γ=90°
Si
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.43070Å b=5.43070Å c=5.43070Å
α=90° β=90° γ=90°
Ge
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.65735Å b=5.65735Å c=5.65735Å
α=90° β=90° γ=90°
C
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=2.456Å b=2.456Å c=6.696Å
α=90° β=90° γ=120°
Sn
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=5.8197Å b=5.8197Å c=3.17488Å
α=90° β=90° γ=90°
S8
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=10.467Å b=12.870Å c=24.493Å
α=90° β=90° γ=90°
He
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.57Å b=3.57Å c=5.83Å
α=90° β=90° γ=120°
Ho
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.5773Å b=3.5773Å c=5.6158Å
α=90° β=90° γ=120°
Li
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.111Å b=3.111Å c=5.093Å
α=90° β=90° γ=120°
La
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.75Å b=3.75Å c=6.07Å
α=90° β=90° γ=120°
Lu
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.5031Å b=3.5031Å c=5.5509Å
α=90° β=90° γ=120°
Na
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.767Å b=3.767Å c=6.154Å
α=90° β=90° γ=120°
Os
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=2.7352Å b=2.7352Å c=4.3190Å
α=90° β=90° γ=120°
Pr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.669Å b=3.669Å c=5.920Å
α=90° β=90° γ=120°
Tb
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.6010Å b=3.6010Å c=5.6936Å
α=90° β=90° γ=120°
Sr
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=4.32Å b=4.32Å c=7.06Å
α=90° β=90° γ=120°
Sc
Wyckoff, R. W. G.
Crystal Structures (1963) 1, 7-83
a=3.3090Å b=3.3090Å c=5.2733Å
α=90° β=90° γ=120°